Nylon 66 Tyre Cord Fabric

(235dtex/1)

(470dtex/1)

(930dtex/1)

(1400dtex/1)

(1870dtex/1)

Ave Breaking strength

N/end

30

30

67

98

127

Elongation at Certain load

%

10±2

10±2

7.5±1.0

7.5±1.0

8.0±1.0

(11.2N)

(22.2N)

(22.6N)

(33N)

(44.1N)

Adhesion(H-test)

N/cm

13

20

49

64

78

Breaking Strength CV

%

5

5

5

5

5

Breaking elongation

%

20+3

20+3

20+2

20+2

20+2

Breaking elongation CV

%

7.5

7.5

7.5

7.5

7.5

Dip pick up

%

4.5+1.5

4.5+1.5

4.5+1.5

4.5+1.5

4.5+1.5

Diameter

mm

0.15+0.03

0.27+0.03

0.32+0.03

0.43+0.03

0.50+0.03

Twist

Single(Z)

T/10cm

35+1.5

21+1.5

21+1.5

19+1.0

16+1.0

Plytwist(S)

/

/

/

/

/

Hot air shrinkage 160℃×2min x 0.05cN/dtex (max)

%

4.5

4.5

4

4

4

Moisture content(max)

%

1

1

0.8

0.8

0.8

(930dtex/2)

(1400dtex/2)

(1870dtex/2)

(2100dtex/2)

Ave Breaking strength

N/en   d

137.2

211.7

280

310

Elongation at certain  load

%

8.5±0.8(44.1 N)

8.5±0.8(66.6N)

8.7±0.8    (88.2N)

9.0±0.8     (100N)

Adhesion (H-test)

N/cm

107.8

137.2

156.8

166.8

Breaking strength CV

%

5.0

5.0

5.0

5.0

Breaking elongation

%

20.5±2

21.5±2

22±2

22±2

Breaking elongation CV

%

7.5

7.5

7.5

7.5

Dip pick up

%

5.0+1.0

5.0+1.0

5.0+1.0

4.5+1.0

Diameter

mm

0.53±0.05

0.65±0.05

0.74±0.05

0.78±0.05

Twist

Single (Z)

T/10cm

46±1.5

37±1.5

32±1.5

32±2.0

Ply twist (S)

46±1.5

37±1.5

32±1.5

32±2.0

Hot air shrinkage160℃×2min x0.05cN/dtex (max)

%

5.0

5.0

5.0

5.5

Moisture content (max)

%

1.0

1.0

1.0

1.0